Record added / Expiration | | SELL | Inclusion (encapsulated) Cadmium Red MY 8002 MY8006
MY8006 MY8002
Inclusion (encapsulated) Red
component: Se-Cd-Si-Zr
Firing stability :up to 1300'c
Application hints :
1 .better results with high refractive index ftitted glaze.
2.best results with no Zinc Oxide,not suitable for Zirconium opacified glaze.
3. Glazes systems containing Alkali metals (<5% weight) improve the color development of pigment inclusion.
4.Component of SiO2 in glazes should below 50% (weight).
5. An appropriate amount of PbO added in the glaze can increase the brightness and lightness of color.
6.To avoid mechanical destruction of inclusion pigment during glaze preparation, we recommend adding the pigment when only 5% of the total milling time remains.
Quantity: 200kg / Transport: shipment | - / shipment / - | 08-26-2006,
283 days left | | SELL | Inclusion (encapsulated)Cadmium Yellow MY6001 MY6003
MY 6001 MY 6002 MY6003
Inclusion (encapsulated) Yellow Golden
component: Zr-Si-Cd
Firing stability:up to 1300'c
Application hints :
1 .better results with high refractive index ftitted glaze.
2.best results with no Zinc Oxide,not suitable for Zirconium opacified glaze.
3. Glazes systems containing Alkali metals (<5% weight) improve the color development of pigment inclusion.
4.Component of SiO2 in glazes should below 50% (weight).
5. An appropriate amount of PbO added in the glaze can increase the brightness and lightness of color.
6.To avoid mechanical destruction of inclusion pigment during glaze preparation, we recommend adding the pigment when only 5% of the total milling time remains.
| - / shipment / - | 08-26-2006,
283 days left | | SELL | Inclusion (encapsulated ) Cadmium Orange MY9001 MY9002
MY9001 MY9002 MY9003
Inclusion (encapsulated )Orange
component: Se-Cd-Zr-Si
firing stability:up to 1300'c (2372'F)
Application hints :
1 .better results with high refractive index ftitted glaze.
2.best results with no Zinc Oxide,not suitable for Zirconium opacified glaze.
3. Glazes systems containing Alkali metals (<5% weight) improve the color development of pigment inclusion.
4.Component of SiO2 in glazes should below 50% (weight).
5. An appropriate amount of PbO added in the glaze can increase the brightness and lightness of color.
6.To avoid mechanical destruction of inclusion pigment during glaze preparation, we recommend adding the pigment when only 5% of the total milling time remains.
| - / shipment / - | 08-26-2006,
283 days left | | SELL | Inclusion(encapsulated) Cadmium Violet MY3001 MY3002
MY3001 MY3002 :Inclusion(encapsulated) Violet
component:Zr-Si-Se-Cd-Co
Firing stability:up to 1300'c
Application hints :
1 .better results with high refractive index ftitted glaze.
2.best results with no Zinc Oxide,not suitable for Zirconium opacified glaze.
3. Glazes systems containing Alkali metals (<5% weight) improve the color development of pigment inclusion.
4.Component of SiO2 in glazes should below 50% (weight).
5. An appropriate amount of PbO added in the glaze can increase the brightness and lightness of color.
6.To avoid mechanical destruction of inclusion pigment during glaze preparation, we recommend adding the pigment when only 5% of the total milling time remains.
| - / shipment / - | 08-26-2006,
283 days left | | SELL | Inclusion(encapsulated) Acid Green MY7001
MY7001 MY7002 :Inclusion(encapsulated) Acid Green
component: Zr-Si-Se-Cd
Firing stability:up to 1250'c
Application hints :
1 .better results with high refractive index ftitted glaze.
2.best results with no Zinc Oxide,not suitable for Zirconium opacified glaze.
3. Glazes systems containing Alkali metals (<5% weight) improve the color development of pigment inclusion.
4.Component of SiO2 in glazes should below 50% (weight).
5. An appropriate amount of PbO added in the glaze can increase the brightness and lightness of color.
6.To avoid mechanical destruction of inclusion pigment during glaze preparation, we recommend adding the pigment when only 5% of the total milling time remains.